Modulation of Noise in Submicron GaAs/AlGaAs Hall Devices by Gating

We present a systematic characterization of fluctuations in submicron Hall devices based on GaAs/AlGaAs two-dimensional electron gas heterostructures at temperatures between 1.5 K to 60 K. A large variety of noise spectra, from 1/f to Lorentzian, are obtained by gating the Hall devices. The noise level can be reduced by up to several orders of magnitude with a moderate gate voltage of 0.2 V, whereas the carrier density increases less than 60% in the same range. The significant dependence of the Hall noise spectra on temperature and gate voltage is explained in terms of the switching processes related to impurities in n-AlGaAs.Comment: 5 pages, 4 fig

Properties and Curie Temperature (130 K) of Heavily Mn-doped Quaternary Alloy Ferromagnetic Semiconductor (InGaMn)As Grown on InP

We have studied magnetic properties of heavily Mn-doped [(In0.44Ga0.56)0.79Mn0.21]As thin films grown by low-temperature molecular-beam epitaxy (LT-MBE) on InP substrates. The (InGaMn)As with high Mn content (21%) was obtained by decreasing the growth temperature to 190 degC. When the thickness of the [(In0.44Ga0.56)0.79Mn0.21]As layer is equal or thinner than 10 nm, the reflection high-energy electron diffraction (RHEED) pattern and transmission electron microscopy (TEM) show no MnAs clustering, indicating that a homogeneous single crystal with good quality was grown. In the magnetic circular dicroism (MCD) measurement, large MCD intensity and high Curie temperature of 130 K were observed.Comment: 3 pages, 5 figure

Effect of high annealing temperature on giant tunnel magnetoresistance ratio of CoFeB/MgO/CoFeB magnetic tunnel junctions

We report tunnel magnetoresistance (TMR) ratios as high as 472% at room temperature and 804% at 5 K in pseudo-spin valve (SV) CoFeB/MgO/CoFeB magnetic tunnel junctions (MTJs) annealed at 450oC, which is approaching the theoretically predicted value. By contrast, the TMR ratios for exchange-biased (EB) SV MTJs with a MnIr antiferromagnetic layer are found to drop when they are annealed at 450oC. Energy dispersive X-ray analysis shows that annealing at 450oC induces interdiffusion of Mn and Ru atoms into the MgO barrier and ferromagnetic layers in EB-SV MTJs. Mechanisms behind the different annealing behavior are discussed.Comment: 13 pages, 5 figure

A spin Esaki diode

We demonstrate electrical electron spin injection via interband tunneling in ferromagnetic/nonmagnetic semiconductor Esaki diodes. An interband tunnel junction between ferromagnetic p+-(Ga,Mn)As and nonmagnetic n+-GaAs under reverse-bias allows spin-polarized tunneling of electrons from the valence band of (Ga,Mn)As to the conduction band of n+-GaAs. The spin polarization of tunneled electrons is probed by circular polarization of electroluminescence (EL) from an n-GaAs/InGaAs/p-GaAs light emitting structure integrated with the diode. Clear hysteresis loop with +-6.5% remanence is observed in the magnetic-field dependence of the EL polarization at 6 K, below the Curie temperature of (Ga,Mn)As.Comment: 11pages, 4figures. Submitted Japanese Journal of Applied Physics Pt2 Express Lette